Cuzn38Sn1As ( CW717R )
| Klas: | Cuzn38Sn1As |
| Nimewo: | CW717R |
| Klasifikasyon: | Cupper alyaj |
| Dansite | 8.4 g/cm ³ |
| Estanda: | EN 1653: 1998 Kwiv ak alyaj kwiv. Plak, fèy ak ti sèk pou chodyèr, veso presyon ak inite depo dlo cho |
| Klas ekivalan: | Ale isit la |
Konpozisyon chimik % klas CuZn38Sn1As (CW717R)
| Fe | Ni | Taks | Kòm | Pb | Sn | Lòt moun | - |
| max 0.1 | max 0.2 | 59 - 62 | 0.02 - 0.06 | max 0.2 | 0.5 - 1 | total 0.2 | Zn - rès |
Pwopriyete mekanik nan klas CuZn38Sn1As (CW717R)
| Rm- Fòs rupture (MPa) (R320) | 320 |
| Rp0.20.2% fòs prèv (MPa) (R320) | 100 |
| A- Min. elongasyon nan ka zo kase (%) (R320) | 30 |
| Vickers dite (HV): (R320) | 80 |
Klas ekivalan klas CuZn38Sn1As (CW717R)
Avètisman! Sèlman pou referans
| Inyon Ewopeyen EN |
ETAZINI - |
Almay DIN,WNr |
Japon JIS |
Lafrans AFNOR |
Angletè BS |
Itali UNI |
Polòy PN |
Tchechi CSN |
Otrich ONORM |
Larisi GOST |
Entèvyou ISO |
||||||||||||
| Cuzn38Sn1As |
|
|
|
|
|
|
|
|
|
|
|
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn38Sn1As (CW717R) alyaj Cupper |