Cuzn37Mn3Al2PSi ( CW713R )
| Klas: | Cuzn37Mn3Al2PSi |
| Nimewo: | CW713R |
| Klasifikasyon: | Konplèks alyaj kwiv-zenk |
| Dansite | 8.1 g/cm³ |
| Estanda: | EN 12164: 1998 Kwiv ak alyaj kwiv. Rod pou rezon D' gratis EN 12167: 1998 Kwiv ak alyaj kwiv. Des ak ba rektangilè pou rezon jeneral EN 12168: 1998 Kwiv ak alyaj kwiv. Hollow baton pou rezon D' gratis EN 12165: 1998 Kwiv ak alyaj kwiv. Fòje ak non forge stock EN 12449: 1999 Kwiv ak alyaj kwiv. San pwoblèm, tib wonn pou rezon jeneral EN 12420: 1999 Kwiv ak alyaj kwiv. Forgings |
| Klas ekivalan: | Ale isit la |
Konpozisyon chimik % klas CuZn37Mn3Al2PbSi (CW713R)
| Fe | sizo | Mn | Ni | al | Taks | Pb | Sn | Lòt moun | - |
| maks 1 | 0.3 - 1.3 | 1.5 - 3 | maks 1 | 1.3 - 2.3 | 57 - 59 | 0.2 - 0.8 | max 0.4 | total 0.3 | Zn - rès |
Pwopriyete mekanik nan klas CuZn37Mn3Al2PbSi (CW713R)
| Rm- Fòs rupture (MPa) (R540) | 540 |
| Rm- Fòs rupture (MPa) (R570) | 570 |
| Rp0.20.2% fòs prèv (MPa) (R540) | 280 |
| Rp0.20.2% fòs prèv (MPa) (R570) | 300 |
| A- Min. elongasyon nan ka zo kase (%) (R540) | 15 |
| A- Min. elongasyon nan ka zo kase (%) (R570) | 12 |
| Brinell dite (HB): (R540) | 150 |
| Brinell dite (HB): (R570) | 150 |
Klas ekivalan klas CuZn37Mn3Al2PbSi (CW713R)
Avètisman! Sèlman pou referans
| Inyon Ewopeyen EN |
Almay DIN,WNr |
||
| Cuzn37Mn3Al2PSi |
|
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn37Mn3Al2PbSi (CW713R) Konplèks alyaj kwiv-zenk |