Cuzn36Sn1Pb ( CW712R )
| Klas: | Cuzn36Sn1Pb |
| Nimewo: | CW712R |
| Klasifikasyon: | Konplèks alyaj kwiv-zenk |
| Dansite | 8.3 g/cm ³ |
| Estanda: | EN 12163: 1998 Kwiv ak alyaj kwiv. Rod pou rezon jeneral EN 12166: 1998 Kwiv ak alyaj kwiv. Fil pou rezon jeneral EN 12167: 1998 Kwiv ak alyaj kwiv. Des ak ba rektangilè pou rezon jeneral EN 12165: 1998 Kwiv ak alyaj kwiv. Fòje ak non forge stock EN 12420: 1999 Kwiv ak alyaj kwiv. Forgings |
| Klas ekivalan: | Pa gen enfòmasyon |
Konpozisyon chimik % klas CuZn36Sn1Pb (CW712R)
| Fe | Ni | Taks | Pb | Sn | Lòt moun | - |
| max 0.1 | max 0.2 | 61 - 63 | 0.2 - 0.6 | 1 - 1.5 | total 0.2 | Zn - rès |
Pwopriyete mekanik nan klas CuZn36Sn1Pb (CW712R)
| Rm- Fòs rupture (MPa) (R340) | 340 |
| Rm- Fòs rupture (MPa) (R460) | 460 |
| Rp0.20.2% fòs prèv (MPa) (R340) | 170 |
| Rp0.20.2% fòs prèv (MPa) (R460) | 340 |
| A- Min. elongasyon nan ka zo kase (%) (R340) | 30 |
| A- Min. elongasyon nan ka zo kase (%) (R460) | 12 |
| Brinell dite (HB): (H080) (R340) | 80 - 120 |
| Brinell dite (HB): (H135) (R460) | 135 |
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn36Sn1Pb (CW712R) Konplèks alyaj kwiv-zenk |