CuZn33Pb2-C (CC750S)
| Klas: | CuZn33Pb2-C |
| Nimewo: | CC750S |
| Klasifikasyon: | Alyaj kwiv-zenk |
| Estanda: | EN 1982: 2008 Kwiv ak alyaj kwiv. Lengote ak depoze |
| Klas ekivalan: | Ale isit la |
Konpozisyon chimik % nan klas CuZn33Pb2-C (CC750S)
| Yo ajoute yon sifiks -C nan deziyasyon an pou idantifye materyèl nan fòm depoze |
| Fe | sizo | Mn | Ni | P | al | Taks | Pb | Sn | - |
| max 0.8 | max 0.05 | max 0.2 | maks 1 | max 0.05 | max 0.1 | 63 - 67 | 1 - 3 | maksimòm 1.5 | Zn - rès; Cu ki gen ladan Ni |
Pwopriyete mekanik nan klas CuZn33Pb2-C (CC750S)
| Rm- Fòs rupture (MPa) (GS) oswa (GZ) | 180 |
| Rp0.20.2% fòs prèv (MPa) (GS) oswa (GZ) | 70 |
| A- Min. elongasyon nan ka zo kase (%) (GS) oswa (GZ) | 12 |
| Brinell dite (HBW): (GS) | 45 |
| Brinell dite (HBW): (GZ) | 50 |
Klas ekivalan klas CuZn33Pb2-C (CC750S)
Avètisman! Sèlman pou referans
| Inyon Ewopeyen EN |
Almay DIN,WNr |
Japon JIS |
Lafrans AFNOR |
Angletè BS |
Itali UNI |
Syèd SS |
Tchechi CSN |
Inter ISO |
|||||||||
| CuZn33Pb2-C |
|
|
|
|
|
|
|
|
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn33Pb2-C (CC750S) alyaj kwiv-zenk |