CuZn28Sn1As ( CW706R )
| Klas: | CuZn28Sn1As |
| Nimewo: | CW706R |
| Klasifikasyon: | Cupper alyaj |
| Dansite | 8.5 g/cm ³ |
| Estanda: | EN 12451: 1999 Kwiv ak alyaj kwiv. San pwoblèm, tib wonn pou echanjeur chalè EN 12452: 1999 Kwiv ak alyaj kwiv. Woule, finned, tib san pwoblèm pou echanjeur chalè |
| Klas ekivalan: | Pa gen enfòmasyon |
Konpozisyon chimik % klas CuZn28Sn1As (CW706R)
| Fe | Mn | Ni | P | Cu | Kòm | Pb | Sn | Lòt moun | - |
| max 0.07 | max 0.1 | max 0.1 | max 0.01 | 70 - 72.5 | 0.02 - 0.06 | max 0.05 | 0.9 - 1.3 | total 0.3 | Zn - rès |
Pwopriyete mekanik nan klas CuZn28Sn1As (CW706R)
| Rm- Fòs rupture (MPa) (R320) | 320 |
| Rm- Fòs rupture (MPa) (R360) | 360 |
| Rp0.20.2% fòs prèv (MPa) (R320) | 100 |
| Rp0.20.2% fòs prèv (MPa) (R360) | 140 |
| A- Min. elongasyon nan ka zo kase (%) (R320) | 55 |
| A- Min. elongasyon nan ka zo kase (%) (R360) | 45 |
| Vickers dite (HV): (H060) (R320) | 60 - 90 |
| Vickers dite (HV): (H080) (R360) | 80 - 110 |
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs traction / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuZn28Sn1As (CW706R) alyaj Cupper |