CuSn8PbP (CW460K)
| Klas: | Cusn8PbP |
| Nimewo: | CW460K |
| Klasifikasyon: | Alyaj kwiv-fèblan |
| Dansite | 8.8 g/cm ³ |
| Estanda: | EN 12449: 1999 Kwiv ak alyaj kwiv. San pwoblèm, tib wonn pou rezon jeneral |
| Klas ekivalan: | Pa gen enfòmasyon |
Konpozisyon chimik % nan klas CuSn8PbP (CW460K)
| Fe | Ni | P | Pb | Zn | Sn | Lòt moun | - |
| max 0.1 | max 0.3 | 0.2 - 0.4 | 0.1 - 0.5 | max 0.3 | 7.5 - 9 | total 0.2 | Cu - rès |
Pwopriyete mekanik nan klas CuSn8PbP (CW460K)
| Rm- Fòs rupture (MPa) (R460) | 460 |
| Rm- Fòs rupture (MPa) (R550) | 550 |
| Rm- Fòs rupture (MPa) (R620) | 620 |
| Rp0.20.2% fòs prèv (MPa) (R460) | 280 |
| Rp0.20.2% fòs prèv (MPa) (R550) | 480 |
| Rp0.20.2% fòs prèv (MPa) (R620) | 540 |
| A- Min. elongasyon nan ka zo kase (%) (R460) | 30 |
| A- Min. elongasyon nan ka zo kase (%) (R550) | 12 |
| A- Min. elongasyon nan ka zo kase (%) (R620) | 5 |
| Vickers dite (HV): (H130) (R460) | 130 - 165 |
| Vickers dite (HV): (H165) (R550) | 165 - 195 |
| Vickers dite (HV): (H180) (R620) | 180 |
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn8PbP (CW460K) alyaj kwiv-fèblan |