CuSn8P (CW459K)
| Klas: | CuSn8P |
| Nimewo: | CW459K |
| Klasifikasyon: | Cupper-fèblan alyaj |
| Dansite | 8.8 g/cm ³ |
| Estanda: | EN 12163: 1998 Kwiv ak alyaj kwiv. Rod pou rezon jeneral EN 12449: 1999 Kwiv ak alyaj kwiv. San pwoblèm, tib wonn pou rezon jeneral |
| Klas ekivalan: | Ale isit la |
Konpozisyon chimik % nan klas CuSn8P (CW459K)
| Fe | Ni | P | Pb | Zn | Sn | Lòt moun | - |
| max 0.1 | max 0.3 | 0.2 - 0.4 | max 0.05 | max 0.3 | 7.5 - 8.5 | total 0.2 | Cu - rès |
Pwopriyete mekanik nan klas CuSn8P (CW459K)
| Rm- Fòs rupture (MPa) (R390) | 390 |
| Rm- Fòs rupture (MPa) (R450) | 450 |
| Rp0.20.2% fòs prèv (MPa) (R390) | 260 |
| Rp0.20.2% fòs prèv (MPa) (R450) | 280 |
| A- Min. elongasyon nan ka zo kase (%) (R390) | 45 |
| A- Min. elongasyon nan ka zo kase (%) (R450) | 26 |
| Brinell dite (HB): (H090) (R390) | 90 - 120 |
| Brinell dite (HB): (H125) (R450) | 125 - 160 |
Klas ekivalan klas CuSn8P (CW459K)
Avètisman! Sèlman pou referans
| Inyon Ewopeyen EN |
Almay DIN,WNr |
||
| CuSn8P |
|
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn8P (CW459K) Cupper-tin alyaj |