CuSn7Pb15-B (CB496K)
| Klas: | CuSN7Pb15-B |
| Nimewo: | CB496K |
| Klasifikasyon: | Alyaj kwiv-fèblan-plon |
| Estanda: | EN 1982: 2008 Kwiv ak alyaj kwiv. Lengote ak depoze |
| Klas ekivalan: | Ale isit la |
Konpozisyon chimik % klas CuSn7Pb15-B (CB496K)
| Yo ajoute yon sifiks -B nan deziyasyon an pou idantifye materyèl nan fòm lengote |
| Fe | sizo | Mn | Ni | P | S | al | Cu | Pb | Zn | Sb | Sn | - |
| max 0.2 | max 0.01 | max 0.2 | 0.5 - 2 | max 0.1 | max 0.08 | max 0.01 | 74 - 79.5 | 13.2 - 17 | maks 2 | max 0.5 | 6.2 - 8 | Cu ki gen ladan Ni |
Pwopriyete mekanik klas CuSn7Pb15-B (CB496K)
| Rm- Fòs rupture (MPa) (GS) | 170 |
| Rm- Fòs rupture (MPa) (GZ) oswa (GC) | 200 |
| Rp0.20.2% fòs prèv (MPa) (GS) | 80 |
| Rp0.20.2% fòs prèv (MPa) (GZ) oswa (GC) | 90 |
| A- Min. elongasyon nan ka zo kase (%) (GS) oswa (GC) | 8 |
| A- Min. elongasyon nan ka zo kase (%) (GZ) | 7 |
| Brinell dite (HBW): (GS) | 60 |
| Brinell dite (HBW): (GZ) oswa (GC) | 65 |
Klas ekivalan klas CuSn7Pb15-B (CB496K)
Avètisman! Sèlman pou referans
| Inyon Ewopeyen EN |
Almay DIN,WNr |
||
| CuSN7Pb15-B |
|
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn7Pb15-B (CB496K) alyaj kwiv-fèblan-plon |