CuSN{0}}.15 ( CW117C )
| Klas: | CuSN{{0}.15 |
| Nimewo: | CW117C |
| Klasifikasyon: | Ba alyaj kwiv alyaj |
| Dansite | 8.9 g/cm³ |
| Estanda: | EN 1758: 1998 Kwiv ak alyaj kwiv. Dezabiye pou ankadreman plon EN 13148: 2001 Kwiv ak alyaj kwiv. Hot-tranpe fèblan teren |
| Klas ekivalan: | Pa gen enfòmasyon |
Konpozisyon chimik % nan klas CuSn0.15 (CW117C)
| Fe | Ni | P | Zn | Sn | Lòt moun | - |
| max 0.02 | max 0.02 | max 0.015 | max 0.1 | 0.1 - 0.15 | total 0.1 | Cu - rès |
Pwopriyete mekanik nan klas CuSn0.15 (CW117C)
| Rm- Fòs rupture (MPa) (R300) | 300-370 |
| Rm- Fòs rupture (MPa) (R360) | 360-430 |
| Rm- Fòs rupture (MPa) (R420) | 420-490 |
| A- Min. elongasyon Lo=50mm (%) (R300) | 4 |
| A- Min. elongasyon Lo=50mm (%) (R360) | 3 |
| A- Min. elongasyon Lo=50mm (%) (R420) | 2 |
| Vickers dite (HV): (H085) | 85 - 110 |
| Vickers dite (HV): (H105) | 105 - 130 |
| Vickers dite (HV): (H120) | 120 - 140 |
Pwopriyete CuSn0.15
| Koefisyan lineyè ekspansyon tèmik=17.3*10(-6) 1/K; Kondiktivite elektrik=47 MS/m; |
Distribisyon pwosesis
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuSn0.15 (CW117C) alyaj kwiv ki ba alyaj |