CuPb1P (CW113C)
| Klas: | CuPb1P |
| Nimewo: | CW113C |
| Klasifikasyon: | Ba alyaj kwiv alyaj |
| Dansite | 8.9 g/cm³ |
| Estanda: | EN 12164: 1998 Kwiv ak alyaj kwiv. Rod pou rezon D' gratis |
| Klas ekivalan: | Ale isit la |
Konpozisyon chimik % klas CuPb1P (CW113C)
| P | Pb | Lòt moun | - |
| 0.003 - 0.012 | 0.7 - 1.5 | total 0.1 | Cu - rès |
Pwopriyete mekanik nan klas CuPb1P (CW113C)
| Rm- Fòs rupture (MPa) (R250) | 250 |
| Rm- Fòs rupture (MPa) (R300) | 300 |
| Rp0.20.2% fòs prèv (MPa) (R250) | 200 |
| Rp0.20.2% fòs prèv (MPa) (R300) | 250 |
| A- Min. elongasyon nan ka zo kase (%) (R250) | 7 |
| A- Min. elongasyon nan ka zo kase (%) (R300) | 5 |
| A- Min. elongasyon Lo=100mm (%) (R250) | 3 |
| A- Min. elongasyon Lo=100mm (%) (R300) | 2 |
| Brinell dite (HB): (R250) | 90 |
| Brinell dite (HB): (R300) | 100 |
Klas ekivalan klas CuPb1P (CW113C)
Avètisman! Sèlman pou referans
| Inyon Ewopeyen EN |
Almay DIN,WNr |
||
| CuPb1P |
|
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs rupture / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuPb1P (CW113C) Low alyaj kwiv alyaj |