CuNi7Zn39Pb3Mn2 ( CW400J )
| Klas: | CuNi7Zn39Pb3Mn2 |
| Nimewo: | CW400J |
| Klasifikasyon: | Alyaj kwiv-nikèl-zenk |
| Dansite | 8.5 g/cm ³ |
| Estanda: | EN 12164: 1998 Kwiv ak alyaj kwiv. Rod pou rezon D' gratis EN 12166: 1998 Kwiv ak alyaj kwiv. Fil pou rezon jeneral EN 12167: 1998 Kwiv ak alyaj kwiv. Des ak ba rektangilè pou rezon jeneral EN 12165: 1998 Kwiv ak alyaj kwiv. Fòje ak non forge stock EN 12420: 1999 Kwiv ak alyaj kwiv. Forgings |
| Klas ekivalan: | Pa gen enfòmasyon |
Konpozisyon chimik % klas CuNi7Zn39Pb3Mn2 (CW400J)
| Fe | Mn | Ni | Taks | Pb | Sn | Lòt moun | - |
| max 0.3 | 1.5 - 3 | 6 - 8 | 47 - 50 | 2.3 - 3.3 | max 0.2 | total 0.2 | Zn - rès |
Pwopriyete mekanik nan klas CuNi7Zn39Pb3Mn2 (CW400J)
| Rm- Fòs rupture (MPa) (R510) | 510 |
| Rp0.20.2% fòs prèv (MPa) (R510) | 400 |
| A- Min. elongasyon nan ka zo kase (%) (R510) | 12 |
| A- Min. elongasyon Lo=100mm (%) (R510) | 8 |
| Brinell dite (HB): (R510) | 150 |
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs traction / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi7Zn39Pb3Mn2 (CW400J) alyaj kwiv-nikèl-zenk |