CuNi12Zn29 (CW405J)
| Klas: | CuNi12Zn29 |
| Nimewo: | CW405J |
| Klasifikasyon: | Cupper alyaj |
| Dansite | 8.6 g/cm³ |
| Estanda: | EN 1654: 1998 Kwiv ak alyaj kwiv. Dezabiye pou sous dlo ak konektè |
| Klas ekivalan: | Pa gen enfòmasyon |
Konpozisyon chimik % nan klas CuNi12Zn29 (CW405J)
| Fe | Mn | Ni | Taks | Pb | Sn | Lòt moun | - |
| max 0.3 | max 0.5 | 11 - 13.5 | 57 - 60 | max 0.03 | max 0.03 | total 0.2 | Zn - rès |
Pwopriyete mekanik nan klas CuNi12Zn29 (CW405J)
| Rm- Fòs rupture (MPa) (R520) | 520-610 |
| Rm- Fòs rupture (MPa) (R600) | 600-690 |
| Rp0.20.2% fòs prèv (MPa) (R520) | 430 |
| Rp0.20.2% fòs prèv (MPa) (R600) | 550 |
| A- Min. elongasyon Lo=50mm (%) (R520) | 3-4 |
| A- Min. elongasyon Lo=50mm (%) (R600) | 2 |
| Vickers dite (HV): (H170) (R520) | 170 - 200 |
| Vickers dite (HV): (H190) (R600) | 190 - 220 |
Pwopriyete CuNi12Zn29
| Modil elastisite=125 kN/mm² Kondiktivite elektrik=4 MS/m; |
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs traction / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuNi12Zn29 (CW405J) alyaj Cupper |