CuAl10Fe5Ni5-C (CC333G)
| Klas: | CuAl10Fe5Ni5-C |
| Nimewo: | CC333G |
| Klasifikasyon: | Alyaj kwiv-aliminyòm |
| Estanda: | EN 1982: 2008 Kwiv ak alyaj kwiv. Lengote ak depoze |
| Klas ekivalan: | Ale isit la |
Konpozisyon chimik % nan klas CuAl10Fe5Ni5-C (CC333G)
| Yo ajoute yon sifiks -C nan deziyasyon an pou idantifye materyèl nan fòm depoze |
| Fe | sizo | Mn | Ni | Kr | al | Taks | Pb | mg | Zn | bi | Sn |
| 4 - 5.5 | max 0.1 | maks 3 | 4 - 6 | max 0.05 | 8.5 - 10.5 | 76 - 83 | max 0.03 | max 0.05 | max 0.5 | max 0.01 | max 0.1 |
Pwopriyete mekanik nan klas CuAl10Fe5Ni5-C (CC333G)
| Rm- Fòs rupture (MPa) (GS) | 600 |
| Rm- Fòs rupture (MPa) (GM) oswa (GZ) oswa (GC) | 650 |
| Rp0.20.2% fòs prèv (MPa) (GS) | 250 |
| Rp0.20.2% fòs prèv (MPa) (GM) oswa (GZ) oswa (GC) | 280 |
| A- Min. elongasyon nan ka zo kase (%) (GS) oswa (GZ) oswa (GC) | 13 |
| A- Min. elongasyon nan ka zo kase (%) (GM) | 7 |
| Brinell dite (HBW): (GS) | 140 |
| Brinell dite (HBW): (GM) oswa (GC) oswa (GZ) | 150 |
Klas ekivalan klas CuAl10Fe5Ni5-C (CC333G)
Avètisman! Sèlman pou referans
| Inyon Ewopeyen EN |
Almay DIN,WNr |
||||||||
| CuAl10Fe5Ni5-C |
|
Pwosesis Distribisyon
| GS | Distribisyon sab |
| GM | Distribisyon mwazi pèmanan |
| GZ | Distribisyon santrifujeur |
| GC | Distribisyon kontinyèl |
| GP | Presyon mouri Distribisyon |
Kondisyon materyèl yo
| R | Kondisyon materyèl ki deziyen pa valè minimòm egzijans fòs rupture pou pwodwi a ak kondisyon fòs rupture obligatwa ak elongasyon |
| H | Kondisyon materyèl ki deziyen pa valè minimòm egzijans dite pou pwodwi a ak kondisyon dite obligatwa |
Pwopriyete mekanik
| ReH | Fòs pwodiksyon minimòm / Mindestwert der oberen Streckgrenze / Limite d elasticite minimale |
| Rm | Fòs traction / Zugfestigkeit / Resistance a la traction |
| A | Allongement minimòm / Mindestwert der Bruchdehnung / Allongement minim |
| J | Notch enpak tès / Kerbschlagbiegeversuch / Essai de flexion par choc |
|
CuAl10Fe5Ni5-C (CC333G) alyaj kwiv-aliminyòm |